PRIMA318LI

Master alloy for the production of yellow 375 – 417 – 585 – 917 ‰ gold jewellery obtained by investment casting. This product, thanks to its complex composition made of numerous different special elements, ensures an extreme level of deoxidation, an extreme surface quality, an enhanced fluidity and a long lasting of this features also after many reuses of casting scraps, making it the most advanced solution for castings with and without stones in place.

375 ‰

417 ‰

585 ‰

Hardness as cast

136 HV

127 HV

125 HV

Density

11.02 g/cm3

11.42 g/cm3

12.83 g/cm3

Melting Range

Solidus: 777 °C
Liquidus: 869 °C

Solidus: 781 °C
Liquidus: 860 °C

Solidus: 797 °C
Liquidus: 856 °C

Description

PRIMA318LI

	375 ‰	417 ‰	585 ‰
Hardness as cast	136 HV	127 HV	125 HV
Density	11.02 g/cm3	11.42 g/cm3	12.83 g/cm3
Melting Range	Solidus: 777 °C Liquidus: 869 °C	Solidus: 781 °C Liquidus: 860 °C	Solidus: 797 °C Liquidus: 856 °C