Master alloy for the production of red 375 – 417 – 585 ‰ gold jewellery obtained by investment casting. The elements contained in this product ensure a high deoxidation in casting and a high surface quality, making it suitable for castings with and without stones in place.

375 ‰

417 ‰

585 ‰

Hardness as cast

103 HV

133 HV

Density

11.1 g/cm3

11.35 g/cm3

12.94 g/cm3

Melting Range

Solidus: 865 °C
Liquidus: 942 °C

Solidus: 865 °C
Liquidus: 938 °C

Solidus: 865 °C
Liquidus: 905.5 °C

Description

SPARK184LG

	375 ‰	417 ‰	585 ‰
Hardness as cast	103 HV	103 HV	133 HV
Density	11.1 g/cm3	11.35 g/cm3	12.94 g/cm3
Melting Range	Solidus: 865 °C Liquidus: 942 °C	Solidus: 865 °C Liquidus: 938 °C	Solidus: 865 °C Liquidus: 905.5 °C