SPARK319

Master alloy for the production of yellow 375 – 417 – 585 – 750 ‰ gold jewellery obtained by investment casting. The elements contained in this product ensure a high deoxidation in casting and a high surface quality, making it suitable for castings with and without stones in place.

375 ‰

417 ‰

585 ‰

750 ‰

Hardness as cast

120 HV

130 HV

140 HV

175 HV

Density

11.2 g/cm3

11.53 g/cm3

13.08 g/cm3

15.47 g/cm3

Melting Range

Solidus: 765 °C
Liquidus: 870 °C

Solidus: 800 °C
Liquidus: 875 °C

Solidus: 795 °C
Liquidus: 850 °C

Solidus: 800 °C
Liquidus: 860 °C

Description

SPARK319

	375 ‰	417 ‰	585 ‰	750 ‰
Hardness as cast	120 HV	130 HV	140 HV	175 HV
Density	11.2 g/cm3	11.53 g/cm3	13.08 g/cm3	15.47 g/cm3
Melting Range	Solidus: 765 °C Liquidus: 870 °C	Solidus: 800 °C Liquidus: 875 °C	Solidus: 795 °C Liquidus: 850 °C	Solidus: 800 °C Liquidus: 860 °C