SPARK695LR

Master alloy for the production of red 585 – 875 – 917 ‰ gold jewellery obtained by investment casting. The elements contained in this product ensure a high deoxidation in casting and a high surface quality, making it suitable for castings with and without stones in place. The use is suggested with the addition of 0 – 20 % of pure silver to the master alloy.

585 ‰

875 ‰

917 ‰

Hardness as cast

130 HV

119 HV

92 HV

Density

12.85 g/cm3

16.6 g/cm3

17.38 g/cm3

Melting Range

Solidus: 900 °C
Liquidus: 920 °C

Solidus: 915 °C
Liquidus: 929 °C

Solidus: 923 °C
Liquidus: 945 °C

Description

SPARK695LR

	585 ‰	875 ‰	917 ‰
Hardness as cast	130 HV	119 HV	92 HV
Density	12.85 g/cm3	16.6 g/cm3	17.38 g/cm3
Melting Range	Solidus: 900 °C Liquidus: 920 °C	Solidus: 915 °C Liquidus: 929 °C	Solidus: 923 °C Liquidus: 945 °C