PLAST696L

Master alloy for the production of red 375 – 417 – 585 ‰ gold jewellery obtained by mechanical working. The elements contained in this product ensure a high surface quality and a high deformation capability thanks the small grain structure, making it suitable for the production of hand and machine made hollow and solid chains, deep drawn items and tube. The use is suggested with the addition of 10 – 20 % of pure silver to the master alloy.

375 ‰

417 ‰

585 ‰

Hardness as cast

114 HV

110 HV

131 HV

Density

11.16 g/cm3

11.48 g/cm3

12.94 g/cm3

Melting Range

Solidus: 821 °C
Liquidus: 935 °C

Solidus: 848 °C
Liquidus: 925 °C

Solidus: 870 °C
Liquidus: 905 °C

Description

PLAST696L

	375 ‰	417 ‰	585 ‰
Hardness as cast	114 HV	110 HV	131 HV
Density	11.16 g/cm3	11.48 g/cm3	12.94 g/cm3
Melting Range	Solidus: 821 °C Liquidus: 935 °C	Solidus: 848 °C Liquidus: 925 °C	Solidus: 870 °C Liquidus: 905 °C