PRIMA220G

Master alloy for the production of white 375 – 417 – 585 – 750 ‰ gold jewellery obtained by investment casting. This product, thanks to its complex composition made of numerous different special elements, ensures an extreme level of deoxidation, an extreme surface quality, an enhanced fluidity and a long lasting of this features also after many reuses of casting scraps, making it the most advanced solution for castings with and without stones in place.

375 ‰

417 ‰

585 ‰

750 ‰

Hardness as cast

123 HV

148 HV

194 HV

Density

10.85 g/cm3

10.88 g/cm3

12.33 g/cm3

14.52 g/cm3

Melting Range

Solidus: 953 °C
Liquidus: 1015 °C

Solidus: 964 °C
Liquidus: 1023 °C

Solidus: 890 °C
Liquidus: 940 °C

Solidus: 884 °C
Liquidus: 907 °C

Description

PRIMA220G

	375 ‰	417 ‰	585 ‰	750 ‰
Hardness as cast	123 HV	123 HV	148 HV	194 HV
Density	10.85 g/cm3	10.88 g/cm3	12.33 g/cm3	14.52 g/cm3
Melting Range	Solidus: 953 °C Liquidus: 1015 °C	Solidus: 964 °C Liquidus: 1023 °C	Solidus: 890 °C Liquidus: 940 °C	Solidus: 884 °C Liquidus: 907 °C