SPARK185LG

Master alloy for the production of red 375 – 417 – 585 ‰ gold jewellery obtained by investment casting. The elements contained in this product ensure a high deoxidation in casting and a high surface quality, making it suitable for castings with and without stones in place.

375 ‰

417 ‰

585 ‰

Hardness as cast

102 HV

120 HV

131 HV

Density

11 g/cm3

11.25 g/cm3

12.94 g/cm3

Melting Range

Solidus: 865 °C
Liquidus: 942 °C

Solidus: 866 °C
Liquidus: 940 °C

Solidus: 865 °C
Liquidus: 908 °C

Description

SPARK185LG

	375 ‰	417 ‰	585 ‰
Hardness as cast	102 HV	120 HV	131 HV
Density	11 g/cm3	11.25 g/cm3	12.94 g/cm3
Melting Range	Solidus: 865 °C Liquidus: 942 °C	Solidus: 866 °C Liquidus: 940 °C	Solidus: 865 °C Liquidus: 908 °C