SPARK666L

Master alloy for the production of yellow 375 – 417 – 585 ‰ gold jewellery obtained by investment casting. The elements contained in this product ensure a high deoxidation in casting and a high surface quality, making it suitable for castings with and without stones in place. The use is suggested with the addition of 0 – 10 % of pure silver to the master alloy.

375 ‰

417 ‰

585 ‰

Hardness as cast

123 HV

118 HV

106 HV

Density

11.02 g/cm3

11.35 g/cm3

12.68 g/cm3

Melting Range

Solidus: 805 °C
Liquidus: 886 °C

Solidus: 803 °C
Liquidus: 884 °C

Solidus: 850 °C
Liquidus: 890 °C

Description

SPARK666L

	375 ‰	417 ‰	585 ‰
Hardness as cast	123 HV	118 HV	106 HV
Density	11.02 g/cm3	11.35 g/cm3	12.68 g/cm3
Melting Range	Solidus: 805 °C Liquidus: 886 °C	Solidus: 803 °C Liquidus: 884 °C	Solidus: 850 °C Liquidus: 890 °C